318C17

2023-05-17 15:48:22 来源：钢铁之家阅读量：0

牌号	318C17
对应标准	BS 3100-1991 一般工程用铸钢件 Specification for Steel castings for general engineering purposes
归类	铸钢
性能	耐腐蚀
标签	奥氏体不锈铸钢有磁性

318C17 化学元素成分含量(%)

成分	C	Si	Mn	P	S	Cr	Ni	Mo	更多
最小值	-	-	-	-	-	17	9	2	Nb:8C~1
最大值	0.08	1.5	2	0.04	0.04	21	-	3	Nb:8C~1

碳当量计算

318C17 机械性能

热处理或状态	抗拉强度 σ_b Mpa	屈服点 σ_s Mpa	断后伸长率或延伸率 δ %
ST(1050°C~1150°C)	≥480	1% proof stress Rp1.0 min ≥240	≥18

A=for anneal by heating to a temperature above the AC3 and cool in the furnace
N=for normalize by heating to a temperature above the AC3 and cool in still air
OQ=for quench into oil from a temperature above the AC3
WQ=for quench into water from a temperature above the AC3
AH=for air harden by heating to a temperature above the AC3 and cool in air at a rate fast enough to produce a hardened microstructure
T=for temper by heating to a temperature below AC1
ST=for solution treat by heating to temperature high enough to dissolve and any intermetallic phases followed by a rapid cool.

近似对照表耐蚀铸钢（不锈钢铸件）

中国	日本	德国		法国	英国
GB	JIS	DIN EN/DIN	W-Nr.	NF EN/NF	BS EN/BS
ZG0Cr18Ni12Mo2Ti	SUS22	G-X10CrNiMoNb 18 10 G-X5CrNiMoNb 18 10	1.4580 1.4581	Z6CNDNb18.12M	318C17