A841 Grades A Class 2

2023-05-17 18:19:13 来源：钢铁之家阅读量：0

牌号	A841 Grades A Class 2
对应标准	ASTM A841/A841M-2017 通过热机械控制工艺生产的压力容器用钢板 Steel Plates for Pressure Vessels, Produced by ThermoMechanical Control Process (TMCP)
归类	合金钢

A841 Grades A Class 2 化学元素成分含量(%)

	成分	C	Si	Mn ^①	P	S	Cr	Ni	Cu	Mo	V	Nb	Al ^②	更多
t≤40mm	最小值	-	0.15	0.7	-	-	-	-	-	-	-	-	0.02	Alt≥0.02或Als≥0.015
t≤40mm	最大值	0.2	0.5	1.35	0.03	0.03	0.25	0.25	0.35	0.08	0.06	0.03	-	Alt≥0.02或Als≥0.015

	成分	C	Si	Mn	P	S	Cr	Ni	Cu	Mo	V	Nb	Al ^②	更多
t＞40mm	最小值	-	0.15	1	-	-	-	-	-	-	-	-	0.02	Alt≥0.02或Als≥0.015
t＞40mm	最大值	0.2	0.5	1.6	0.03	0.03	0.25	0.25	0.35	0.08	0.06	0.03	-	Alt≥0.02或Als≥0.015

① Manganese may exceed 1.35 % on heat analysis, up to a maximum of 1.60 %, provided that the carbon equivalent on heat analysis does not exceed 0.47 %, or the value specified in Supplementary Requirement S77 when that requirement is invoked, when based on the following formula：
CE = C+Mn/6+(Cr+Mo+V)/5+(Ni+Cu)/15%
When this option is exercised, the manganese content on product analysis shall not exceed the heat analysis content by more than 0.12 percentage points.
② By agreement, the steel may be produced with titanium, in which case the minimum aluminum content shall not apply. When this option is exercised, the titanium content, by heat analysis, shall be .006 % to 0.02 %, and the actual titanium content shall be reported on the test report.

碳当量计算

A841 Grades A Class 2 机械性能

	抗拉强度 σ_b Mpa	屈服点 σ_s Mpa	断后伸长率或延伸率 δ %
t≤65	550~690	≥415	(50mm) ≥22
t＞65	515~655	≥380	≥22

注：本资料来源于互联网的公开资源整理，我们不保证这些资料的准确性、完整性和适用性。这些资料仅供您参考，不应用于任何商业用途或决策依据。本资料所记载的技术信息是说明产品的代表性特点和性能的参考值，对于因误用或不当使用本资料所记载的信息等而造成的损害恕难承担责任，敬请周知。